Characterization of P3HT:thermoplastic blends prepared via direct-ink writing
Thèse ou mémoire / Thesis or Dissertation
Date de publication
Autrices et auteurs
Identifiant ORCID de l’auteur
Contributrices et contributeurs
Direction de recherche
Publié dans
Date de la Conférence
Lieu de la Conférence
Éditeur
Cycle d'études
Maîtrise / Master's
Programme
Affiliation
Mots-clés
- Mélanges de polymères
- Optoélectronique
- Direct-ink writing
- P3HT
- Thermoplastique
- Fabrication additive
- Impression 3D assistée par évaporation de solvant
- Polymer blends
- Optoelectronic
- Thermoplastic
- 3D printing
Organisme subventionnaire
Résumé
Résumé
Les dispositifs optoélectroniques sont devenus un élément essentiel de la technologie moderne visant à exploiter des applications de niche pour l'électronique flexible à base de composés organiques. Jusqu'à présent, les films minces préparés à partir de composés polymères conjugués ont été les principaux concurrents pour les dispositifs optoélectroniques organiques. Avec l'apparition de nouvelles méthodes de mise en œuvre et de nouveaux besoins électroniques, les méthodes de fabrication additive des matériaux optoélectroniques suscitent de plus en plus d'intérêt. Malgré l'intérêt croissant et la variété des méthodes de mise en œuvre tridimensionnelles, on comprend encore mal l'impact de la technique de mise en œuvre sur l'organisation moléculaire des échantillons. Ici, une étude est présentée impliquant l’impression 3D assistée par évaporation de solvant et le poly(3-hexylthiophène) (P3HT) qui est bien décrit dans la littérature, et, dans ce cas-ci, mélangé à diverses matrices thermoplastiques. Dans un premier temps, les matrices thermoplastiques employées, i.e. le polystyrène (PS), le polypropylène carbonate (PPC), le polyméthacrylate de méthyle (PMMA) et le polyoxyéthylène (PEO) sont évaluées en fonction de leurs propriétés rhéologiques et de leur imprimabilité en 3D, qui ne sont que très peu affectées par l'introduction du P3HT. Par la suite, le P3HT à régiorégularité élevée et faible est mélangé dans chacune des matrices thermoplastiques. L'organisation moléculaire des deux composantes dans les architectures imprimées a été évaluée par des techniques de spectroscopie UV-visible et de fluorescence. Les phases en présence ont été analysées à l'aide d’analyse calorimétrique différentielle à balayage, de microscopie optique polarisée et de diffraction des rayons X, ce qui a également permis d'analyser l'état d'agrégation du P3HT par rapport à celui retrouvé dans les films minces. Il est intéressant de noter que les propriétés optiques montrent peu ou pas de différence entre les architectures 3D et les films minces, ce qui indique vraisemblablement que l'efficacité d'un dispositif optoélectronique imprimé en 3D ne serait pas affectée par l’impression 3D assistée par évaporation de solvant. Cette étude pourrait permettre de mieux comprendre comment il serait possible de mettre au point des dispositifs optoélectroniques, y compris des photoconducteurs, des photovoltaïques organiques, des transistors à effet de champ organiques, etc. à l’aide de techniques de fabrication additive, ce qui ouvrira la voie à une nouvelle ère en électronique organique imprimée en trois dimensions.
Optoelectronic devices have become a staple in modern day technology which aims to transition to flexible electronics that are developed from organic compounds. To date, 2-dimensional films of conjugated polymer compounds have been the main contender for organic optoelectronic devices. As new processing methods and electronic needs become present in the modern day, a focus on 3-dimensional processing methods of optoelectronic materials have become increasingly of interest. With the increasing interest and variety of 3-dimensional processing methods, there is little understanding of how the processing technique molecularly affects the final product. Herein is presented a study on the extrusion-based, direct-ink writing of the well understood poly(3-hexylthiophene-2,5-diyl) (P3HT) blended into a variety of thermoplastic matrices. Initially the pristine thermoplastics of polystyrene (PS), poly(propylene carbonate) (PPC), poly(methyl methacrylate) (PMMA), and poly(ethylene oxide) (PEO) were evaluated based on their rheological and printable properties which are negligibly affected by the introduction of P3HT. Subsequently, after the blending of both high and low regioregular P3HT into each of the thermoplastic matrices, the printed architectures were further analyzed by X-Ray diffraction, UV-vis, and fluorescence techniques to assess the aggregation state of P3HT in comparison to 2-dimensional processed films. Interestingly, the electronic properties show little to no difference between 3-dimensional architectures and 2-dimensional films, which presumably indicates that the efficiency would not be affected by the direct-ink writing technique. This study could contribute to the beginning of producing optoelectronic devices, including photoconductors, organic photovoltaic and organic field effect transistors, in 3-dimensions resulting in a new age of electronics.
Optoelectronic devices have become a staple in modern day technology which aims to transition to flexible electronics that are developed from organic compounds. To date, 2-dimensional films of conjugated polymer compounds have been the main contender for organic optoelectronic devices. As new processing methods and electronic needs become present in the modern day, a focus on 3-dimensional processing methods of optoelectronic materials have become increasingly of interest. With the increasing interest and variety of 3-dimensional processing methods, there is little understanding of how the processing technique molecularly affects the final product. Herein is presented a study on the extrusion-based, direct-ink writing of the well understood poly(3-hexylthiophene-2,5-diyl) (P3HT) blended into a variety of thermoplastic matrices. Initially the pristine thermoplastics of polystyrene (PS), poly(propylene carbonate) (PPC), poly(methyl methacrylate) (PMMA), and poly(ethylene oxide) (PEO) were evaluated based on their rheological and printable properties which are negligibly affected by the introduction of P3HT. Subsequently, after the blending of both high and low regioregular P3HT into each of the thermoplastic matrices, the printed architectures were further analyzed by X-Ray diffraction, UV-vis, and fluorescence techniques to assess the aggregation state of P3HT in comparison to 2-dimensional processed films. Interestingly, the electronic properties show little to no difference between 3-dimensional architectures and 2-dimensional films, which presumably indicates that the efficiency would not be affected by the direct-ink writing technique. This study could contribute to the beginning of producing optoelectronic devices, including photoconductors, organic photovoltaic and organic field effect transistors, in 3-dimensions resulting in a new age of electronics.
Table des matières
Notes
Notes
Autre version linguistique
Ensemble de données lié
Licence
Approbation
Évaluation
Complété par
Référencé par
Ce document diffusé sur Papyrus est la propriété exclusive des titulaires des droits d'auteur et est protégé par la Loi sur le droit d'auteur (L.R.C. (1985), ch. C-42). Sauf si le document est diffusé sous une licence Creative Commons, il ne peut être utilisé que dans le cadre d'une utilisation équitable et non commerciale comme le prévoit la Loi (i.e. à des fins d'étude privée ou de recherche, de critique ou de compte-rendu). Pour toute autre utilisation, une autorisation écrite des titulaires des droits d'auteur sera nécessaire.